UTP A Celsit 706 V
Outstanding alloy against abrasion, thermo-shock and corrosion combined with high temperatures. The weld deposit can be machined with tungsten tool tips and by grinding. The hardness of the weld deposit will degrees 16% at 300°C and about 30% at 600°C. The weld deposit is high heat resistant up to 900°C. DUR 6 offers a low coefficient of friction of 0.12 and exceptional resistance to galling. It has cavitation-erosion resistance ten times that of 304 stainless steel, DUR 6 can be used to protect bearing surfaces in non-lubricating conditions due to its resistance to metal-to-metal wear.
Not required
Steam-valves, high temperature liquid pumps, hot cutting tools, exhaust valves.
Steam-valves, high temperature liquid pumps, hot cutting tools, exhaust valves.
Outstanding alloy against abrasion, thermo-shock and corrosion combined with high temperatures. The weld deposit can be machined with tungsten tool tips and by grinding. The hardness of the weld deposit will degrees 16% at 300°C and about 30% at 600°C. The weld deposit is high heat resistant up to 900°C. DUR 6 offers a low coefficient of friction of 0.12 and exceptional resistance to galling. It has cavitation-erosion resistance ten times that of 304 stainless steel, DUR 6 can be used to protect bearing surfaces in non-lubricating conditions due to its resistance to metal-to-metal wear.
Stellite 6 alloy for, Steam-valves, high temperature liquid pumps, hot cutting tools, exhaust valves and seats
| Heat Treatment |
RP0,2 (MPa) |
Rm (MPa) |
A5 (%) |
Hardness |
|---|---|---|---|---|
| As Welded | 40 HRc |
Uitstekende legering tegen slijtage, thermische schok en corrosie in combinatie met hoge temperaturen. De neersmelt kan worden bewerkt met wolfraam gereedschappunten en door slijpen. De hardheid van de neersmelt wordt 16% minder bij 300°C en ongeveer 30% bij 600°C. Uitstekende legering tegen thermische schokken, abrasie, erosie, corrosie en cavitatie bij hoge temperaturen.
140°C / 24 hr
Uitstekende legering tegen slijtage, thermische schok en corrosie in combinatie met hoge temperaturen. De neersmelt kan worden bewerkt met wolfraam gereedschappunten en door slijpen. De hardheid van de neersmelt wordt 16% minder bij 300°C en ongeveer 30% bij 600°C. Uitstekende legering tegen thermische schokken, abrasie, erosie, corrosie en cavitatie bij hoge temperaturen.
ER CoCr-A
Stellite 6
| Heat Treatment |
RP0,2 (MPa) |
Rm (MPa) |
A5 (%) |
Hardness |
|---|---|---|---|---|
| As Welded | 43 HRc |